點(diǎn)擊圖片查看大圖聚丙烯腈-丁二烯-乙烯(ABS)熱塑性樹脂被廣泛認(rèn)為是一種優(yōu)良的工程材料，具有卓越的美學(xué)、流動(dòng)性、韌性、空間穩(wěn)定性和耐高溫性。CYCOLAC樹脂的廣泛組合的成績提供platability VISUALFX™美學(xué),高溫,醫(yī)療兼容性,加上國內(nèi)外符合監(jiān)管和安全標(biāo)準(zhǔn)。高光澤等級(jí)提供了增強(qiáng)的美感。
CYCOLAC ™ Resin MG47F
多用途、注塑ABS，提供了良好的工程性能平衡。FDA兼容。
產(chǎn)品物性表：
| Property |
| TYPICAL PROPERTIES (1) | ||||
| MECHANICAL | Value | Unit | Standard | |
| Tensile Stress, yld, Type I, 5 mm/min | 440 | kgf/cm2 | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 330 | kgf/cm2 | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 2 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 24 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 23100 | kgf/cm2 | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 710 | kgf/cm2 | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 23400 | kgf/cm2 | ASTM D 790 | |
| Hardness, Rockwell R | 112 | - | ASTM D 785 | |
| Tensile Stress, yield, 50 mm/min | 47 | MPa | ISO 527 | |
| Tensile Stress, break, 50 mm/min | 35 | MPa | ISO 527 | |
| Tensile Strain, yield, 50 mm/min | 2.6 | % | ISO 527 | |
| Tensile Strain, break, 50 mm/min | 25 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 2370 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 70 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 2200 | MPa | ISO 178 | |
| IMPACT | Value | Unit | Standard | |
| Izod Impact, notched, 23°C | 32 | cm-kgf/cm | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 305 | cm-kgf | ASTM D 3763 | |
| Izod Impact, notched 80*10*4 +23°C | 22 | kJ/m2 | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 8 | kJ/m2 | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 26 | kJ/m2 | ISO 179/1eA | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 9 | kJ/m2 | ISO 179/1eA | |
| THERMAL | Value | Unit | Standard | |
| Vicat Softening Temp, Rate B/50 | 99 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 94 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 80 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 8.82E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 8.82E-05 | 1/°C | ASTM E 831 | |
| Vicat Softening Temp, Rate B/50 | 98 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 100 | °C | ISO 306 | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 81 | °C | ISO 75/Af | |
| Relative Temp Index, Elec | 60 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 60 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 60 | °C | UL 746B | |
| PHYSICAL | Value | Unit | Standard | |
| Specific Gravity | 1.04 | - | ASTM D 792 | |
| Mold Shrinkage, flow, 3.2 mm (5) | 0.5 - 0.8 | % | SABIC Method | |
| Melt Flow Rate, 230°C/3.8 kgf | 5.6 | g/10 min | ASTM D 1238 | |
| Melt Viscosity, 240°C, 1000 sec-1 | 2250 | poise | ASTM D 3825 | |
| Density | 1.04 | g/cm3 | ISO 1183 | |
| Melt Flow Rate, 220°C/10.0 kg | 18 | g/10 min | ISO 1133 | |
| ELECTRICAL | Value | Unit | Standard | |
| Arc Resistance, Tungsten {PLC} | 6 | PLC Code | ASTM D 495 | |
| Hot Wire Ignition {PLC) | 3 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 3 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 0 | PLC Code | UL 746A | |
| Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A | |
| FLAME CHARACTERISTICS | Value | Unit | Standard | |
| UL Recognized, 94HB Flame Class Rating (3) | 1.5 | mm | UL 94 | |
| Source GMD, last updated:2016/03/07 |
| Processing |
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 - 95 | °C |
| Drying Time | 2 - 4 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.1 | % |
| Melt Temperature | 220 - 260 | °C |
| Nozzle Temperature | 220 - 260 | °C |
| Front - Zone 3 Temperature | 215 - 240 | °C |
| Middle - Zone 2 Temperature | 205 - 225 | °C |
| Rear - Zone 1 Temperature | 190 - 210 | °C |
| Mold Temperature | 50 - 70 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Shot to Cylinder Size | 50 - 70 | % |
| Vent Depth | 0.038 - 0.051 | mm |
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們原則上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買/賣家，交易前請?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請向環(huán)球塑化網(wǎng)舉報(bào)。